D3 steel also knows as DIN 1.2080 and JIS SKD1, which is a 12% chrome alloy steel. JIS SKD1 steel has very high wear resistance against abrasive and adhesive wear due to the high volume of hard carbides in the steel matrix, medium toughness, dimensionally stable, high compressive strength, not secondary hardenable. D3 steel composition and more information as below.
| SKD1 Steel Round Bar Sheet Plate Supply | |||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Type | Specification | Surface | |||||||||||||||||
| Round Bar | Dia: 20-600mm;
Length: 5800mm, 40ft container; Other specifications can be customized. | Original Black, Peeled, Machined/Turned, Polished/ Grounded/Milled/Grinded | |||||||||||||||||
| Sheet/Plate/Slab | Thickness: 10-600mm; Width: 30-810mm;
Length: same as above; Other specifications can be customized. | Original Black, Peeled, Machined/Turned, Polished/ Grounded/Milled/Grinded | |||||||||||||||||
D3 Steel Grade Equivalent Chart
| Country | USA | Germany/UK/France | JAPAN | ISO |
|---|---|---|---|---|
| Standard | ASTM A681-08 ALLOY TOOL STEEL | EN ISO 4957: 1999 TOOL STEEL | JIS G4404: 2006 ALLOY TOOL STEEL | ISO 4957: 1999 TOOL STEEL |
| Grades | D3 | X210Cr12/1.2080 | SKD1 | X210Cr12 |
D3 Steel Chemical Composition
| STAND | C(%) | Mn(%) | P(%) | S(%) | Si(%) | Cr(%) | V(%) | W(%) |
|---|---|---|---|---|---|---|---|---|
| ASTM A681-08 | 2.00-2.35 | 0.10-0.60 | ≤0.030 | ≤0.030 | 0.10-0.60 | 11.00-13.50 | ≤1.00 | ≤1.00 |
| JIS G4404: 2006 | 1.40-1.60 | ≤0.60 | ≤0.030 | ≤0.030 | 0.40 | 11.00-13.00 | 0.20-0.50 | - |
| EN ISO 4957:1999 | 1.90-2.20 | 0.20-0.60 | - | - | 0.10-0.60 | 11.00-13.00 | - | - |
| ISO 4957: 1999 | 1.90-2.20 | 0.20-0.60 | - | - | 0.10-0.60 | 11.00-13.00 | - | - |
1.2080 Steel Physical Properties
| Physical Properties | Metric | Imperial |
|---|---|---|
| Density | 7.7 x 1000 kg/m3 | 0.278 lb/in3 |
| Melting Point | 1421°C | 2590°F |
D3 Steel Mechanical Properties
| Mechanical Properties | Metric | Imperial |
|---|---|---|
| Izod impact unnotched | 28.0 J | 20.7 ft-lb |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30457 ksi |
Hot Sale Products
SKD1 Steel Application
1.Highly stressed cutting
2.Punching tools for thin sheet
3.Blanking and forming dies
4.Forming rolls
5.Drawing and deep drawing tools
6.Slitting Knife
7.Stone processing tools
8.Pressure pads
9.Thermosetting plastic molding
D3 Steel Round Bar Sheet Plate Heat Treatment
Heat Treatment
SKD1 steel requires hardening and tempering to achieve maximum properties. For maximum accuracy, the parts of SKD1 tool steel should be stress relieved after roughing operations. Stress should be relieved at 648°C (1200°F) for one hour and cooled slowly.
Annealing
Annealing of SKD1 steel needs to be done in a controlled atmosphere furnace. D3 steels should be heated thoroughly to 871°C (1600°F) and cooled slowly at a rate of not more than -6°C (20°F) per hour, until the furnace is black. Then the material should be removed and air cooled.
Tempering
The SKD1 steel should be cooled to room temperature and should be tempered immediately. The parts should be placed in the tempering furnace and increased slowly to the desired tempering temperature. Tempering for 1 hour per inch of thickness is required.
Hardening
SKD1 steel should be heated properly since it is very sensitive to overheating and if not heated maximum hardness cannot be achieved. The work should be directly placed in a furnace preheated to 954°C (1750°F) and soaked for 20-25 minutes, plus 5 minutes per inch of thickness, and then oil-quenched to harden it.
SKD1 Related Steel Equivalent Property
D3 Steel
Annealing Hardness ≤ 255HB, Cold Drawing Hardness ≤ 269HB
SKD1 Steel
Annealing Temperature830-880℃, Slow Cooling
Annealing Hardness ≤ 255HB
Quenching in 1030 ℃, Air Cooling, Tempering in 180 ℃
Notice
Other specifications are determined by daily stock. Customization is also acceptable.
We are a professional special steel stockist and supplier with a high-quality stand for many years. Please contact us for any request of D3 tool steels materials. Songshun Steel always with you.
Our Advantage
Manufacturing
With 7000 tons of hydraulic forging press, electric slag furnace and other high-end production equipment, we produce a great variety of steels with the best quality in China.
Testing
In order to control the quality, we have complete testing methods to make sure satisfy the customer needs, including Chemical Analysis, Ultrasonic Test and so on.
Massive Stock
We keep a mass stock are over 20000 tons for various steel type, including steel round bar, steel sheet, alloy steel, carbon steel, stainless steel, mold steel, steel coil and etc.
Customized Service
With a professional steel engineers team, we provide customized service according to your project drawing, also provide professional project experience for your special project, such as materials, processing conditions and etc.
World Wide Delivery
For container shipment, standard packing and bundle round bar and flat bar would be applied. It is necessary to fasten & reinforcement would be done to ensure the safety and better unloading at the destination port.
For less than container shipment, wooden box package would be applied for different size materials. For milled or grounded materials, the anti-rust oil would be needed to ensure the surface condition, within the wooden box.